Summary of Technical Specifications
Parameter | PFG-01* | VRP-M** | PFG-03M | PFG-03C | PFG-04 |
Holographic Sensitivity | |||||
@ 457nm CW microJoules/cm2 | 2000 | 80000 | |||
@ 488nm CW microJoules/cm2 | 100000 | ||||
@ 514.5nm CW microJoules/cm2 | 75 | 3000 | 250000 | ||
@ 526.5nm 30ns pulse with latensification - microJoules/cm2 | 75 | ||||
@ 633nm microJoules/cm2 | 100 | 1500-2000 | 3000 | ||
Gamma | >6.0 | >6.0 | >6.0 | >6.0 | x |
Max Density on Characteristic Curve (Dmax) | <4.0 | <4.0 | <4.0 | <4.0 | x |
Fog Density (D0) | <0.01 | <0.01 | <0.01 | <0.01 | x |
Resolving Power (R), mm-1 | 3000 | >5000 | >5000 | Grainless | |
Max. of Spectral Sensitization, nm | 633 | 530 | 633 | 457/514/633 | 415 |
Swollen Emulsion Layer Strenght after Chemical Processing, H (gm force) | 900 | 900 | >50 | >50 | x |
Adhesion between Emulsion Layer and Base after chemical processing (Class A-F). | A-C | A-C | A-C | A-C | x |
Deformation Temperature of Emulsion Layer in water (tdef), °C | >90°C | >90°C | >35°C | >35°C | x |
Emulsion Layer Thickness (microns) | 7 to 8 | 6 to 7 | 6 to 7 | 9 to 10 | 16 to 17 |
Normal Diffraction Efficiency for Reflection | |||||
@ 457nm, % | >25% | >75% | |||
@ 488nm, % | >75% | ||||
@ 514.5nm, % | 40% | ||||
@ 526.5nm, % | 40% | ||||
@ 633nm, % | >40% | >45% | >45% | ||
Geola Guaranteed Storage Period At 4 Degrees Celsius, 30% Humidity. | |||||
Film Roll (months) | 18 | 18 | 18 | x | x |
Cut Sheets (months) | 12 | 12 | 6 | x | x |
Plates (months) | 18 | 18 | 12 | 12 | 12 |